Molecular-weight Dependent Tg Depression of Silica-supported Poly(alpha-methyl styrene) Films

The glass transition temperature ($T_g$) of poly($\alpha$-methyl styrene) (P$\alpha$MS) films supported by silica is studied as a function of film thicknesses from ~17 to ~168 nm at three molecular weights of 1.3, 20 and 420 kg/mol. For the 20 and 420 kg/mol films, the glass transition temperature decreases with decreasing film thickness, consistent with previous results. But for the 1.3 kg/mol films, it becomes independent of the film thickness. We tentatively suggest the $T_g$ depression to be caused by free volume excess at the polymer-air interface and that its influence diminishes at low enough molecular weights because of a chain stiffness effect.